Product description
參數
牌號( Shop sign): ZG-P-493/ZG-I-338
 
低硬度,低密度,聚醚型鞋墊鞋底原液
 
1.特性:低硬度,低密度,聚醚型
 
Characteristics:Low hardness,low density,Polyether insoles.
 
2.用途:適用於聚醚鞋墊的生產
 
Application:Applicable for the production of polyether insoles for men and women.
 
 
 
3. 原液特性Typical properties of PU Resin
 
品名 外觀 粘度(Pa·s/50℃) 密度(g/cm3/40℃) 包裝(kg)
ZG-P-493 白色或淡黃,液狀無異物White or pale yellow, liquid, no foreign material 0.30-0.70 1.00-1.05 18
ZG-I-338
透明液體無異物Transparent liquid, no foreign material 0.10-0.30 1.00-1.05 20
 
參考發貨配比(Reference shipments ratio):A/B=33/20(桶)
 
Reference shipments ratio: A/B=33/20(barrel)
 
測試項目Test item 參考物性值Reference physical properties
鞋底成型密度Molded density of sole(g/cm3 0.3-0.4
硬度(A型)Hardness (type A) 10-25
拉伸強度Tensile strength(MPa) 2.0-3.0
伸長率Elongation(%) 350-550
NBS耐磨NBS abrasion resistance(%) ≥10%
自由泡密度Free foam density(g/cm3 0.22-0.36
耐折性(常溫)(4萬次裂口長度,mm)Folding endurance (room temperature)(40,000 gap length mm) <8
 
4. 成型條件及物性值(Molding conditions & physical properties):
 
 
●配合比率是以最佳配比值為基礎,此配比值會隨添加的顏料助劑種類和添加量不同而變化。
 
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
 
●自由泡沫密度會依季節(溫度,濕度)的不同而變化。
 
Free foam density will vary with the seasons (temperature, humidity).
 
●脫模時間會隨成型品厚度的增加而延長。
 
Stripping time will be extended with the increase of the thickness of moldings.
 
●耐折條件:屈撓角度為 90度,頻率為80次/min*4萬次。
 
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
 
● 以上數據僅作參考,具體數據以實際操作為準。如需其他物性指標,請與我公司聯係。
 
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.